2025 Controlling fibrinogen adsorption on polyelectrolyte multilayer films by modifying self-assembly conditions

Authors:
Borislava Borisova,Sonia Apostolova,Irina Georgieva,Marina Ivanova,Rumen Krastev,Rumiana Tzoneva,Tonya Andreeva

Journal:
Colloids and Surfaces B: Biointerfaces, Volume 254, October 2025, 114821; DOI: 10.1016/j.colsurfb.2025.114821

Institute:

TUM School of Engineering and Design, Department of Materials Engineering, Technical University of Munich, Boltzmannstraße 15, 85748 Garching, Germany

Center for Protein Assemblies (CPA) and Munich Institute of Biomedical Engineering (MIBE), Technical University of Munich, Ernst-Otto-Fischer Straße 8, Garching, Germany

Abstract:

This study investigates the relationship between fibrinogen adsorption on polyelectrolyte multilayer (PEM) films and their surface properties. The films were constructed using weak polyelectrolytes, poly(acrylic acid) (PAA), and poly(allylamine hydrochloride) (PAH), with polyethyleneimine (PEI) as a precursor layer. Different deposition conditions, such as pH levels (3.5 and 7.0) and the type of outermost layer (PAA or PAH), were used to create films with tunable hydrophilicity and surface charge. The thickness of these films was measured using ellipsometry, and surface wettability was assessed via the contact angle method. Fibrinogen adsorption was quantified using quartz crystal microbalance with dissipation monitoring (QCM-D) and enzyme immunoassay (EIA) method, focusing on its D-domain exposure concerning surface thrombogenicity. Results indicated that PEM films are generally hydrophilic. Among them, PAH, the outermost layer, is the least hydrophilic and, therefore, has the lowest surface energy. Film thickness varied with the pH of the solutions, creating a mechanism to control layer parameters. Fibrinogen adsorption was more pronounced on less hydrophilic surfaces, which were thinner, viscoelastic, more hydrated, and preferentially positively charged. These findings suggest that by controlling surface properties, one can enhance hemocompatibility by influencing fibrinogen adsorption and subsequent platelet adhesion and activation.